Knife steel sheet hardened (420) 1000 x 360 mm
" The advantages of this steel are its good wear resistance and minimal internal stress. With a Rockwell hardness of 49-53 HRC, this material is ideal for gauges, tools and machine knives in the food industry and scalpels. This special steel is corrosion-resistant in moist air, steam and water and should not be welded if possible, since the martensitic chrome steels are air-hardening. The material 1.4034 is magnetizable and can therefore be clamped on the magnetic clamping plates of grinding machines. Other uses/properties: Sawing in the food industry Fabric knife Wear rails Print Crackers Brake discs very well etchable magnetisable "
Special Steel - 420 + 1% Mo - hardened ca.300 x 1000mm
The advantages of this steel are its good wear resistance and minimal internal tension. With a tensile strength of 1700 to 1950 N / mm², this material is ideal for springs, gauges, tools and knives.This special steel is corrosion-resistant in moist air, in water vapor and in water, is suitable for high mechanical loads and has a high fatigue strength. The material 420 + 1% Mo is magnetizable and can therefore be clamped on magnetic chucks of grinding machines Further applications / properties: Knives and saws in the food industry Scalpels textile knife wear strips Shock absorbers and leaf valves for compressors Very easy to etch magnetizable
Hardened sheet steel tool 1075 + Cr 1000 x 350 mm
With this material, a small addition of chromium leads to a higher wear resistance and better through-hardening with large cross-sections.a The material 1075 + Cr is magnetisable and can therefore be easily clamped on the magnetic clamping plates of grinding machines. Due to the high carbon content of around 0.75%, material 1075 + Cr should not be welded. Mild steels are not resistant to corrosion. When used in a normal environment, these steels must be protected against corrosion with paint, tinning or zinc plating. Additional properties: suitable for smaller tools magnetisable
Content: 0.35 m² (€130.23 / 1 m²)
Chromium steel sheet ~430 ca.300 mm x 1000mm
"This stainless chromium steel has very good heat resistance and is very well suited as a heat conductor and is used in exhaust gas treatment. This ferritic steel is also used for stainless metal foils that are supposed to be magnetizable. The material is very easy to weld. Other properties very well etchable magnetizable very easy to weld "
Rust-resistant spring steel Alloy 926 (hard) ca.400 x 1000mm
Due to a molybdenum addition of 6.0 to 6.5% and an increased nickel content of over 24%, this material is extremely corrosion-resistant and suitable for many applications in the food industry as well as environmental and partly in medical technology. The material Alloy 926 is seawater resistant, even at elevated temperatures in heat exchangers and at elevated salt concentrations such as in desalination plants. Since this material is almost non-magnetizable even in the hard-rolled state, it can be used for components that are exposed to strong magnetic fields. The importance of Alloy 926 stainless steel in modern industry cannot be underestimated. Its unique properties have made it an indispensable material in various industries. From chemical processing to shipbuilding to the automotive industry, Alloy 926 has proven to meet the demands of demanding applications. The exceptional corrosion resistance of Alloy 926 enables operators of chemical plants to make their production processes more efficient and safer. In the automotive industry, it helps improve vehicle performance and durability. And in shipbuilding, it enables the construction of ships that can withstand the harsh conditions of the seas. Overall, stainless steel Alloy 926 has proven that it is far more than just ordinary stainless steel. Its unique properties make it a valuable material that is indispensable in various industries. The history of Alloy 926 is one of success and innovation, and it will continue to play an important role in modern industry. Further application examples: Components in phosphoric acid production Components for the bleaching stage in the pulp industry Pressure vessels in the temperature range from -196 to 400° Celsius Tanks for storing and transporting aggressive chemical substances Building authority approval for components and fasteners in the indoor area of swimming pools (approved by the German Institute for Structural Engineering, September 1998) The material 1.4529 is not listed in DIN EN 10 151 as a spring material.
Carbon Sheet 1095 ca.300 x 1000mm
Sheet - Foil of Carbon steel (C- Steel) Precision sheets / underlay made of carbon steel 1095 (C100S) - 1.1274 are used among others in mechanical engineering as underlay foils, for aligning workpieces in grinding machines or for setting and measuring gap dimensions. Properties material 1.1274 With a carbon content of over 1%, this material is very well suited for feeler gauges and underlay foils as well as for highly stressed springs, which are not subject to any corrosion requirements. Compared to the materials 1.1231 (C67S), 1.1248 (C75S) and 1.1269 (C85S), which have a lower carbon content, the material 1.1274 is also suitable for high mechanical loads and has a high fatigue strength. Technical information The thickness tolerance is defined according to DIN EN 9445 table 1 or T3. The material 1.1274 is magnetizable and can therefore be clamped on magnetic chucks of grinding machines. The structure of the strip is changed by the hardening process. This means that the rolling direction does not have to be taken into account when edging. Bending radius: at least 10 times the strip thickness. The unalloyed steels must be estimated from corrosion by an oil film. Tinning or galvanizing or painting these steels can withstand corrosion permanently. Further applications / properties: Wear strips Printing racks very easy to etch magnetizable
Carbon Steel unhardened 1075 300 x 1000 mm
This uncured carbon steel is easy to harden and is very well suited for springs and wearing parts to which no claims regarding corrosion are made. The material 1075 can be magnetised and can therefore be clamped very well on magnetic clamping plates of grinding machines. With a high carbon content of about 0.75%, this carbon steel should not be welded. Unalloyed steels must be protected against corrosion by an oil film. Permanently, these steels can withstand corrosion by tinning, galvanizing or painting. Next properties: very good punching and forming (in unhardened state) very good etchable magnetizable hardenable
Sheet steel DC04 unalloyed (1.0338) approx. 300 mm x 1000 mm
Non-alloyed steels are very low-cost materials for simple parts with no demands on corrosion resistance and mechanical loads. As a rule, this special grade (DC04) is used, for example, for simple automotive parts both indoors and outdoors. The material DC 04 is magnetizable and can therefore be clamped very well on magnetic clamping plates of surface grinding machines. This steel is not corrosion resistant and must be protected against corrosion by galvanizing, tinning, chrome plating or painting. Further Applications / Properties: body panels furniture fittings painted sheet metal panels very good etchable very good weldability suitable for punching
Laser Cutting
Laser parts - laser cutting - inquire online Individual product production of laser cutting parts according to your specifications. With a sketch, a drawing or a DXF file you can use our online form to inquire, request a quote and order. We manufacture for both private and business customers. We cut individual pieces or small series for you up to a size of 20 x 40cm (other dimensions on request) from sheet metal 0.05 - 2mm thick (other dimensions on request). Various materials such as stainless steel, copper, brass, bronze etc. can be processed with our lasers.