Precision feeler gauge tape
Precision tapes or metal foils made of spring steel CrNi - hard steel - 301 are used inter alia. in mechanical engineering as underlay foils, for aligning workpieces in grinding machines, adjusting games (assembly of workpieces) or measuring gap dimensions.
Properties material 301
With this material, high strength is achieved by cold rolling. Compared to material 301, a much higher tensile strength can be achieved.
Therefore, the material is very well suited for stainless precision gauges and shims as well as for stainless springs and parts with higher strength.
Due to the alloy with chrome and nickel, this spring steel has good corrosion resistance. Material 1.4404 should be used in a corrosive environment.
If no special requirements are placed on corrosion, the material 1.1274 can also be used.
Technical information
The thickness tolerance is defined according to DIN EN 9445 table 1 or T3 (for strength class 15-1700 N / mm²).
Like other austenitic stainless steels, this steel is very easy to weld. However, the heat input at the weld seam can lead to a structural change (which reduces the strength) and, among other things, local corrosion of the weld seam.
With material 301, when bending or bending, make sure that the bends should always run across the rolling direction. When used as a flat spring, the rolling direction must also be observed.
Further technical information on our cold-rolled spring steel 301 can be found in our data sheet.
Further applications / properties:
- Welded endless belts
- conveyor belts
- very easy to etch
- weakly magnetizable
- good corrosion resistance
| Material: | Spring Steel |
| Thickness: | 0,005 mm |
| Length: | 5000 mm |
| Width: | 12,7 mm |
| DIN Material - Name: | X10CrNi18-8 |
| Material - Number: | 1.4310 |
| ASTM/AISI (USA): | 301 |
| Surface: | 2H |
| Delivery - State: | hard |
| Norm: | DIN 10204 |
| Magnetisable: | weakly |
| Structure: | cold rolled (austenitic with parts of forming martensite), not hardenable |
| Thickness Tolerance: | DIN EN 9445 Table 1 or T3 (for strength class 15-1700 N/mm²) |
| Tensile Strenght: | >1500 N/mm² |
Der Shop mit der großen Auswahl
Ich habe das, was ich schon länger suche, hier gefunden.
Astreine Qualität
Der Stahl läßt sich gut aus der Kassette entnehmen, ablängen und bearbeiten. Seine Kanten sind sauber rechtwinklig, mäßig scharf also, und gratfrei. Er behält einen Teil der Biegung durch das Aufrollen bei; mir fehlt das genaue Wissen, wie sich das Material nach Entnahme am besten begradigen / entspannen läßt, aber das war für meine Anwendung irrelevant.
Preis/Leistung und Lieferzeit erstklassig.
Freue mich insgesamt sehr, für meinen etwas spezielleren Anwendungsfall dieses Produkt hier gefunden zu haben und werde sehr gerne weiterhin hier einkaufen.
gut
Prima Ware
Top
Sehr gute und schnelle Service.
Zeitnahe Lieferung. Gute Ware. Das passt.
Zeitnahe Lieferung. Gute Ware. Das passt.
Große Asortimänt
sehr gut
was ist mit "Zusammenfassung" gemeint?
Top-Qualität,, praktische Box für Aufbewahrung und Entnahme von Teilstücken, sehr gutes Preis-Leistungsverhältnis. Bin mit dem Produkt rundum zufrieden.
alles prima, Ware 1A
alles prima, Ware 1A